Refractory linings are built with bricks and special shapes. There are a vast number of shapes and compositions to meet a wide-range of furnace design requirements. Those refractory products that are supplied in their final form are called shaped refractories. Bricks and special shapes are the backbone of the refractory industry and can be either fired, or chemically or resin bonded.
The processes involved in shaping include pressing, ramming, and vibrating. Standard, rectangular-shaped bricks are adequate dor building straight walls. Other shapes are required for building furnaces with curved walls or roofs. To build these, bricks are shaped into arcs, wedges, radial, and circular standard forms. Togni maintains a close relationship with its clients so i can adapt its products to the shapes that are required for specific applications. |
|
|
 |
|
| |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
MgO |
CaO |
SiO2 |
Fe2O3 |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| BASITOG-B |
98,5 |
0,7 |
0,1 |
0,5 |
2,90 |
16,5 |
50 |
10 |
| BASITOG-BHT |
97,5 |
0,8 |
0,4 |
0,6 |
2,97 |
15,0 |
65 |
16 |
| BT-95 |
94,8 |
2,0 |
1,0 |
1,2 |
2,85 |
16,8 |
72 |
14 |
| BASITOG |
90,0 |
4,0 |
2,0 |
2,0 |
2,80 |
19,0 |
70 |
13 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
MgO |
CaO |
SiO2 |
C |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| BT-2068-B |
98,5 |
0,7 |
0,1 |
5,0 |
2,95 |
5,0 |
65 |
18 |
| BASITOG-CA-B |
98,5 |
0,7 |
0,1 |
9,0 |
2,90 |
4,0 |
60 |
16 |
| BT-1990 |
98,5 |
0,7 |
0,1 |
13,0 |
2,85 |
4,0 |
60 |
16 |
| BT-1991 |
98,5 |
0,6 |
0,1 |
13,0 |
2,90 |
3,0 |
50 |
16 |
| BASITOG-CAB-50 |
98,2 |
0,3 |
0,3 |
9,0 |
2,95 |
3,5 |
70 |
18 |
| BTM-75 |
96,0 |
1,6 |
0,6 |
5,0 |
2,90 |
4,0 |
60 |
17 |
| BTM-50 |
94,0 |
2,5 |
1,2 |
5,0 |
2,80 |
7,0 |
60 |
11 |
| BASITOG-CA-5 |
90,0 |
4,0 |
2,0 |
5,0 |
2,70 |
5,0 |
70 |
15 |
| BASITOG-CA |
90,0 |
4,0 |
2,0 |
8,0 |
2,76 |
6,0 |
60 |
12 |
| BASITOG-CA-13 |
90,0 |
4,0 |
2,0 |
13,0 |
2,75 |
5,3 |
50 |
14 |
| BASITOG-CA-17 |
90,0 |
4,0 |
2,0 |
17,0 |
2,80 |
4,1 |
50 |
13 |
| BT-065 |
90,1 |
0,1 |
1,3 |
10,0 |
2,96 |
5,0 |
48 |
12 |
| (*) Análise química da magnésia / Chemical analysis of magnesia |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
MgO |
CaO |
SiO2 |
Fe2O3 |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| BASITOG-BE |
94,0 |
0,6 |
0,3 |
0,5 |
2,95 |
15,0 |
60 |
13 |
| BT-95-E |
89,5 |
2,0 |
1,0 |
1,2 |
2,85 |
18,8 |
55 |
11,5 |
| BASITOG-E |
85,0 |
3,8 |
1,9 |
2,3 |
2,80 |
20,0 |
50 |
10 |
| BASITOG-EE |
85,0 |
3,8 |
1,9 |
2,3 |
2,80 |
20,0 |
45 |
9 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
MgO |
Cr2O3 |
Fe2O3 |
SiO2 |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| MACRO-2775 |
84,2 |
4,9 |
4,3 |
2,6 |
2,86 |
18,0 |
50 |
10 |
| MACRO-3674 |
70,3 |
14,7 |
6,7 |
0,5 |
3,13 |
15,5 |
62 |
10 |
| MACRO-2680 |
66,0 |
15,0 |
11,0 |
2,0 |
3,05 |
17,0 |
70 |
11 |
| MACRO-3774 |
62,7 |
19,7 |
9,4 |
1,8 |
3,10 |
15,5 |
70 |
10 |
| MACRO-MAG-RH-M |
60,0 |
18,5 |
8,5 |
2,0 |
3,15 |
15,0 |
60 |
12 |
| MACRO-MAG-RH |
59,0 |
18,0 |
9,3 |
2,2 |
3,15 |
15,0 |
60 |
12 |
| MACRO-2526 |
59,0 |
20,0 |
8,5 |
2,4 |
3,15 |
16,0 |
75 |
12 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
Fe2O3 |
Na2O+K2O |
ZrO2 |
C |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| VG-1964 (*) |
94,0 |
0,2 |
0,4 |
- |
6,0 |
3,10 |
14,0 |
70 |
14 |
| VGT-2674-A |
94,0 |
0,2 |
0,2 |
4,0 |
- |
3,10 |
17,0 |
75 |
18 |
| VGT-95 |
93,0 |
0,3 |
0,3 |
- |
- |
3,10 |
16,0 |
120 |
20 |
| VGW-95 |
93,0 |
0,3 |
0,4 |
- |
- |
3,15 |
15,0 |
120 |
15 |
| (*) Análise química base calcinada / Chemical analysis calcined basis |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| T-3254/B |
99,0 |
0,2 |
0,2 |
0,6 |
3,15 |
17,6 |
68 |
15 |
| CTW-95 |
93,0 |
6,0 |
0,3 |
0,4 |
3,15 |
15,0 |
95 |
20 |
| T-92 |
92,0 |
5,0 |
0,8 |
0,3 |
3,00 |
19,0 |
80 |
15 |
| T-86 |
86,0 |
11,0 |
1,2 |
0,4 |
3,00 |
18,0 |
60 |
13 |
| T-85-U |
85,5 |
11,5 |
1,7 |
0,3 |
2,80 |
18,0 |
70 |
15 |
| T-85 |
84,5 |
11,5 |
1,8 |
0,6 |
2,80 |
18,0 |
65 |
13 |
| T-82 |
82,0 |
15,5 |
1,0 |
0,5 |
2,70 |
16,5 |
80 |
15 |
| T-81 |
81,0 |
14,5 |
1,8 |
0,5 |
2,75 |
20,0 |
65 |
12 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
Cr2O3 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| ALUCROM-90-WBP |
90,0 |
4,0 |
0,5 |
0,4 |
3,15 |
13,0 |
100 |
20 |
| ALUCROM-90-BP |
90,0 |
4,0 |
0,4 |
0,4 |
3,15 |
15,0 |
90 |
20 |
| ALUCROM-80-BP |
82,0 |
4,0 |
0,9 |
0,5 |
3,00 |
13,0 |
85 |
20 |
| ALUCROM-3254 |
81,1 |
10,4 |
0,5 |
0,1 |
3,20 |
14,0 |
110 |
40 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
Fe2O3 |
Na2O+K2O |
C |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| ALUCARB-2181/2 |
95,6 |
0,6 |
0,2 |
6,5 |
3,05 |
10,0 |
90 |
20 |
| ALUCARB-2255/B |
83,0 |
2,1 |
0,8 |
7,0 |
2,75 |
11,5 |
70 |
20 |
| MULCARB |
71,0 |
2,0 |
0,9 |
8,5 |
2,45 |
13,0 |
40 |
9 |
| (*) Análise química base calcinada / Chemical analysis calcined basis |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
Fe2O3 |
Na2O+K2O |
C |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| ALUCARB-E |
88,0 |
0,5 |
0,3 |
6,5 |
3,15 |
6,0 |
70 |
20 |
| ALUCARB-BE |
81,9 |
0,6 |
0,2 |
6,5 |
2,86 |
9,9 |
57 |
16 |
| (*) Análise química base calcinada / Chemical analysis calcined basis |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiC |
Fe2O3 |
C |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| ALSIC-3009 (*) |
87,5 |
7,5 |
0,5 |
7,0 |
3,10 |
5,0 |
70 |
15 |
| ALSIC-018/B (*) |
87,5 |
6,8 |
0,3 |
14,0 |
2,98 |
8,1 |
37 |
15 |
| ALSIC-3122 (*) |
84,5 |
7,5 |
0,5 |
7,0 |
3,10 |
6,0 |
80 |
15 |
| ALSIC--C-70 (*) |
79,0 |
15,5 |
0,8 |
6,0 |
3,00 |
5,0 |
90 |
15 |
| ALSIC-3539 (*) |
76,3 |
7,5 |
1,5 |
7,0 |
2,95 |
7,5 |
50 |
15 |
| ALSIC-70 |
73,0 |
14,0 |
1,5 |
- |
2,80 |
19,0 |
80 |
10 |
| (*) Análise química base calcinada / Chemical analysis calcined basis |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| T-2659 |
74,5 |
24,8 |
0,2 |
0,1 |
2,46 |
15,9 |
63 |
23 |
| MTA |
72,3 |
26,9 |
0,2 |
0,5 |
2,50 |
17,0 |
60 |
13 |
| MTW |
71,5 |
27,0 |
0,9 |
0,3 |
2,60 |
15,0 |
90 |
15 |
| MT-72 |
70,0 |
27,0 |
1,2 |
0,5 |
2,50 |
17,0 |
50 |
12 |
| MZ-100 |
66,8 |
13,2 |
0,1 |
19,6(ZrO2) |
3,15 |
18,0 |
50 |
12 |
| MZ-3151 |
62,0 |
22,0 |
0,2 |
15,0(ZrO2) |
2,80 |
15,0 |
80 |
20 |
| MZ-053 |
51,6 |
16,2 |
0,1 |
31,7(ZrO2) |
3,00 |
17,0 |
95 |
23 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| QL-92-V |
90,0 |
8,0 |
0,6 |
0,7 |
3,20 |
10,0 |
80 |
20 |
| QL-85 |
84,0 |
11,0 |
2,0 |
1,0 |
2,85 |
11,0 |
60 |
12 |
| QL-85-A |
82,0 |
8,8 |
1,4 |
0,5 |
2,87 |
11,0 |
60 |
10 |
| QL-81 |
80,0 |
16,0 |
1,2 |
0,8 |
2,90 |
8,5 |
60 |
10 |
| QL-71 |
70,0 |
25,0 |
2,0 |
1,0 |
2,45 |
14,0 |
40 |
7 |
| QL-61 |
61,5 |
32,5 |
2,0 |
1,2 |
2,40 |
12,0 |
50 |
13 |
| QL-2468/9 |
53,9 |
39,5 |
2,0 |
1,1 |
2,40 |
13,0 |
59 |
10 |
| QL-45 |
53,0 |
34,1 |
2,0 |
1,3 |
2,40 |
12,0 |
50 |
10 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| QL-85-Q |
84,0 |
10,0 |
2,0 |
1,0 |
2,75 |
19,0 |
55 |
13 |
| QL-71-Q |
70,0 |
20,4 |
2,0 |
0,8 |
2,40 |
20,0 |
80 |
20 |
| QL-61-Q |
62,0 |
32,0 |
2,0 |
1,2 |
2,35 |
15,0 |
50 |
13 |
| QL-45-Q |
56,0 |
38,0 |
2,4 |
1,3 |
2,30 |
15,0 |
60 |
15 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| S-72 |
75,0 |
17,0 |
1,9 |
0,7 |
2,50 |
18,0 |
75 |
18 |
| S-70 |
72,0 |
23,0 |
1,6 |
0,8 |
2,50 |
16,5 |
70 |
18 |
| T-73 |
70,7 |
24,0 |
1,8 |
1,0 |
2,50 |
19,0 |
61 |
13 |
| TS-75 |
64,7 |
33,6 |
0,8 |
0,5 |
2,61 |
15,5 |
60 |
11 |
| T-2598 (*) |
63,0 |
34,0 |
0,9 |
0,5 |
2,55 |
15,0 |
80 |
14 |
| T-62 |
61,0 |
33,5 |
2,2 |
0,9 |
2,35 |
18,0 |
70 |
13 |
| T-55 |
57,0 |
37,0 |
1,9 |
1,2 |
2,35 |
15,0 |
60 |
14 |
| TAF |
55,0 |
38,0 |
1,8 |
0,7 |
2,35 |
13,9 |
80 |
18 |
| TBF |
54,9 |
40,5 |
1,0 |
1,0 |
2,36 |
15,0 |
60 |
12 |
| PB-1-G |
53,9 |
40,0 |
2,2 |
1,5 |
2,20 |
22,0 |
35 |
8 |
| T-50 |
53,0 |
42,0 |
2,0 |
1,2 |
2,30 |
14,0 |
70 |
15 |
| T-51 |
52,0 |
42,0 |
2,1 |
1,3 |
2,30 |
17,0 |
60 |
12 |
| CT-2 |
52,0 |
42,0 |
2,2 |
1,3 |
2,25 |
18,0 |
50 |
15 |
| T-45 |
50,0 |
44,0 |
2,0 |
1,2 |
2,30 |
14,0 |
70 |
15 |
| (*) Alta resistência ao Creep Test / High Creep Test resistence |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| KALDAS (*) |
49,2 |
48,4 |
0,8 |
0,4 |
2,38 |
14,0 |
62 |
11 |
| T-3117 (*) |
47,0 |
48,0 |
1,2 |
0,5 |
2,35 |
14,5 |
60 |
12 |
| SA-42 |
45,9 |
48,8 |
1,8 |
1,2 |
2,13 |
21,7 |
36 |
6 |
| CT-1 |
43,7 |
51,8 |
1,3 |
1,1 |
2,05 |
20,0 |
35 |
10 |
| (*) Alta resistência ao Creep Test / High Creep Test resistence |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
Ataque por Ácido Sulfúrico
Attack by Sulfuric Acid |
Ataque por Ácido Clorídrico
Attack by Hydrochloric Acid |
| |
Al2O3 |
SiO2 |
TiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
(%) |
(%) |
| CTRA-1 |
34,4 |
58,0 |
1,5 |
1,6 |
3,8 |
2,16 |
3,0 |
100 |
19 |
0,2 |
1,8 |
| CTRA-2 |
43,2 |
51,9 |
- |
1,5 |
1,5 |
2,30 |
8,0 |
90 |
- |
4,5 |
0,3 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Porosidade Aparente
Apparent Porosity |
Resistência à Compressão
Cold Crushing Strength |
Resistência à Flexão
Cold Modulus of Rupture |
| |
Al2O3 |
SiO2 |
Fe2O3 |
Na2O+K2O |
(g/cm³) |
(%) |
(MPa) |
(MPa) |
| T-023 |
25,7 |
70,2 |
0,8 |
2,4 |
2,06 |
12,0 |
50 |
7 |
| SA-4 |
29,9 |
65,0 |
1,5 |
2,5 |
2,04 |
21,0 |
25 |
3 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão
Cold Crushing Strength |
Condutividade Térmica (W/m.K)
Thermal Conductivity (W/m.K) |
Temperatura Máxima de Utilização
Maximum Recommended Service Temperature |
| |
Al2O3 |
Fe2O3 |
(g/cm³) |
(MPa) |
500ºC | 800ºC | 1100ºC | 1400ºC | (ºC) |
| IV-6 |
17,7 |
7,4 |
0,60 |
2 |
0,29 |
0,30 |
- |
- |
800 |
| RI-1206 |
45,5 |
1,1 |
0,60 |
0,9 |
0,19 |
0,26 |
0,35 |
- |
1 200 |
| RI-1308 |
45,5 |
1,1 |
0,80 |
2 |
0,30 |
0,31 |
0,37 |
- |
1 300 |
| RI-1310 |
45,5 |
1,1 |
1,00 |
3 |
0,35 |
0,38 |
0,50 |
- |
1 300 |
| RI-1413 |
45,5 |
0,5 |
1,30 |
8 |
0,94 |
0,94 |
1,02 |
1,19 |
1 400 |
| RI-1414 |
45,5 |
0,5 |
1,40 |
12 |
1,05 |
0,99 |
1,08 |
1,31 |
1 400 |
| RI-1415 |
45,5 |
0,5 |
1,50 |
15 |
1,05 |
1,03 |
1,10 |
1,23 |
1 400 |
| RI-1515 |
65,5 |
0,9 |
1,50 |
25 |
1,06 |
1,03 |
1,08 |
1,22 |
1 500 |
| RI-1416 |
45,5 |
0,5 |
1,60 |
25 |
1,08 |
1,08 |
1,16 |
1,32 |
1 400 |
|
|
|
| |
|
|
|